| Physical Properties |
Metric |
English |
Comments |
| Density |
1.78 g/cc |
0.0643 lb/in³ |
| Water Absorption |
<= 0.0400 % |
<= 0.0400 % |
| Linear Mold Shrinkage |
0.0200 - 0.0300 cm/cm |
0.0200 - 0.0300 in/in |
Melt Flow  |
2.00 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
2.00 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| |
6.00 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
6.00 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Shore D |
72.0
@Thickness 2.00 mm |
72.0
@Thickness 0.0787 in |
| Tensile Strength, Ultimate |
20.0 - 40.0 MPa |
2900 - 5800 psi |
| Tensile Strength, Yield |
20.0 - 35.0 MPa |
2900 - 5080 psi |
| Elongation at Break |
200 - 600 % |
200 - 600 % |
| Elongation at Yield |
10.0 - 12.0 % |
10.0 - 12.0 % |
| Modulus of Elasticity |
1.05 GPa |
152 ksi |
| Flexural Modulus |
0.900 GPa |
131 ksi |
| Flexural Yield Strength |
37.0 MPa |
5370 psi |
| Coefficient of Friction |
0.200 - 0.300 |
0.200 - 0.300 |
| Coefficient of Friction, Static |
0.200 - 0.400 |
0.200 - 0.400 |
| Taber Abrasion, mg/1000 Cycles |
5.00 - 15.0 |
5.00 - 15.0 |
| Izod Impact, Notched |
1.70 J/cm
@Thickness 4.00 mm,
Temperature 23.0 °C |
3.18 ft-lb/in
@Thickness 0.157 in,
Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
>= 1.00e+14 ohm-cm |
>= 1.00e+14 ohm-cm |
| Surface Resistance |
>= 1.00e+14 ohm |
>= 1.00e+14 ohm |
| Dielectric Constant |
7.00
@Frequency 1e+6 Hz |
7.00
@Frequency 1e+6 Hz |
| |
| Thermal Properties |
Metric |
English |
Comments |
| Heat of Fusion |
35.0 J/g |
15.1 BTU/lb |
| |
38.0 J/g |
16.3 BTU/lb |
| CTE, linear |
140 - 160 µm/m-°C
@Temperature 20.0 °C |
77.8 - 88.9 µin/in-°F
@Temperature 68.0 °F |
| Specific Heat Capacity |
1.20 J/g-°C |
0.287 BTU/lb-°F |
| |
1.60 J/g-°C
@Temperature 100 °C |
0.382 BTU/lb-°F
@Temperature 212 °F |
| Thermal Conductivity |
0.190 W/m-K |
1.32 BTU-in/hr-ft²-°F |
| Melting Point |
160 °C |
320 °F |
| Crystallization Temperature |
122 °C |
252 °F |
| Maximum Service Temperature, Air |
330 - 350 °C |
626 - 662 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
100 °C
@Thickness 4.00 mm |
212 °F
@Thickness 0.157 in |
| Deflection Temperature at 1.8 MPa (264 psi) |
52.0 °C
@Thickness 4.00 mm |
126 °F
@Thickness 0.157 in |
| Vicat Softening Point |
150 °C
@Load 1.00 kg,
Thickness 4.00 mm |
302 °F
@Load 2.20 lb,
Thickness 0.157 in |
| Brittleness Temperature |
-18.0 °C |
-0.400 °F |
| Glass Transition Temp, Tg |
-29.0 °C |
-20.2 °F |
| Flammability, UL94 |
V-0 |
V-0 |
| Oxygen Index |
44.0 - 65.0 %
@Thickness 3.00 mm |
44.0 - 65.0 %
@Thickness 0.118 in |