Physical Properties |
Metric |
English |
Comments |
Density |
1.83 g/cc |
0.0661 lb/in³ |
Water Absorption |
<= 0.0700 % |
<= 0.0700 % |
Linear Mold Shrinkage |
0.0100 - 0.0300 cm/cm |
0.0100 - 0.0300 in/in |
Melt Flow |
2.00 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.00 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
6.00 g/10 min @Load 5.00 kg, Temperature 230 °C |
6.00 g/10 min @Load 11.0 lb, Temperature 446 °F |
|
Mechanical Properties |
Metric |
English |
Comments |
Hardness, Shore D |
82.0 @Thickness 2.00 mm |
82.0 @Thickness 0.0787 in |
Tensile Strength, Ultimate |
40.0 - 60.0 MPa |
5800 - 8700 psi |
Tensile Strength, Yield |
56.0 - 60.0 MPa |
8120 - 8700 psi |
Elongation at Break |
20.0 - 30.0 % |
20.0 - 30.0 % |
Elongation at Yield |
3.00 - 5.00 % |
3.00 - 5.00 % |
Modulus of Elasticity |
4.20 GPa |
609 ksi |
Flexural Modulus |
4.50 GPa |
653 ksi |
Flexural Yield Strength |
89.0 MPa |
12900 psi |
Coefficient of Friction |
0.200 - 0.300 |
0.200 - 0.300 |
Coefficient of Friction, Static |
0.200 - 0.400 |
0.200 - 0.400 |
Taber Abrasion, mg/1000 Cycles |
5.00 - 10.0 |
5.00 - 10.0 |
Izod Impact, Notched |
0.600 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
1.12 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
|
Electrical Properties |
Metric |
English |
Comments |
Electrical Resistivity |
>= 1.00e+14 ohm-cm |
>= 1.00e+14 ohm-cm |
Surface Resistance |
<= 1000 ohm |
<= 1000 ohm |
|
Thermal Properties |
Metric |
English |
Comments |
Heat of Fusion |
59.0 J/g |
25.4 BTU/lb |
|
67.0 J/g |
28.8 BTU/lb |
CTE, linear |
120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
Thermal Conductivity |
0.300 W/m-K |
2.08 BTU-in/hr-ft²-°F |
Melting Point |
174 °C |
345 °F |
Crystallization Temperature |
140 °C |
284 °F |
Maximum Service Temperature, Air |
300 - 350 °C |
572 - 662 °F |
Deflection Temperature at 0.46 MPa (66 psi) |
152 °C @Thickness 4.00 mm |
306 °F @Thickness 0.157 in |
Deflection Temperature at 1.8 MPa (264 psi) |
156 °C @Thickness 4.00 mm |
313 °F @Thickness 0.157 in |
Vicat Softening Point |
168 °C @Load 1.00 kg, Thickness 4.00 mm |
334 °F @Load 2.20 lb, Thickness 0.157 in |
Brittleness Temperature |
>= 0.000 °C |
>= 32.0 °F |