Physical Properties |
Metric |
English |
Comments |
Density |
1.78 g/cc |
0.0643 lb/in³ |
Water Absorption |
<= 0.0400 % |
<= 0.0400 % |
Linear Mold Shrinkage |
0.0200 - 0.0300 cm/cm |
0.0200 - 0.0300 in/in |
Melt Flow |
2.00 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.00 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
6.00 g/10 min @Load 5.00 kg, Temperature 230 °C |
6.00 g/10 min @Load 11.0 lb, Temperature 446 °F |
|
Mechanical Properties |
Metric |
English |
Comments |
Hardness, Shore D |
60.0 @Thickness 2.00 mm |
60.0 @Thickness 0.0787 in |
Tensile Strength, Ultimate |
30.0 - 50.0 MPa |
4350 - 7250 psi |
Tensile Strength, Yield |
15.0 - 18.0 MPa |
2180 - 2610 psi |
Elongation at Break |
600 - 750 % |
600 - 750 % |
Elongation at Yield |
12.0 - 15.0 % |
12.0 - 15.0 % |
Modulus of Elasticity |
0.360 - 0.480 GPa |
52.2 - 69.6 ksi |
Flexural Modulus |
0.360 - 0.440 GPa |
52.2 - 63.8 ksi |
Coefficient of Friction |
0.200 - 0.300 |
0.200 - 0.300 |
Coefficient of Friction, Static |
0.200 - 0.400 |
0.200 - 0.400 |
Taber Abrasion, mg/1000 Cycles |
5.00 - 15.0 |
5.00 - 15.0 |
Izod Impact, Notched |
1.80 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
3.37 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
|
Electrical Properties |
Metric |
English |
Comments |
Electrical Resistivity |
>= 1.00e+14 ohm-cm |
>= 1.00e+14 ohm-cm |
Surface Resistance |
>= 1.00e+14 ohm |
>= 1.00e+14 ohm |
|
Thermal Properties |
Metric |
English |
Comments |
Heat of Fusion |
23.0 J/g |
9.89 BTU/lb |
|
24.0 J/g |
10.3 BTU/lb |
CTE, linear |
150 - 180 µm/m-°C @Temperature 20.0 °C |
83.3 - 100 µin/in-°F @Temperature 68.0 °F |
Specific Heat Capacity |
1.20 J/g-°C |
0.287 BTU/lb-°F |
|
1.60 J/g-°C @Temperature 100 °C |
0.382 BTU/lb-°F @Temperature 212 °F |
Thermal Conductivity |
0.180 W/m-K |
1.25 BTU-in/hr-ft²-°F |
Melting Point |
135 °C |
275 °F |
Crystallization Temperature |
92.0 °C |
198 °F |
Maximum Service Temperature, Air |
330 - 350 °C |
626 - 662 °F |
Deflection Temperature at 0.46 MPa (66 psi) |
62.0 °C @Thickness 4.00 mm |
144 °F @Thickness 0.157 in |
Deflection Temperature at 1.8 MPa (264 psi) |
40.0 °C @Thickness 4.00 mm |
104 °F @Thickness 0.157 in |
Vicat Softening Point |
120 °C @Load 1.00 kg, Thickness 4.00 mm |
248 °F @Load 2.20 lb, Thickness 0.157 in |
Brittleness Temperature |
-22.0 °C |
-7.60 °F |
Glass Transition Temp, Tg |
-29.0 °C |
-20.2 °F |
Oxygen Index |
44.0 % @Thickness 3.00 mm |
44.0 % @Thickness 0.118 in |