| Physical Properties |
Metric |
English |
Comments |
| Density |
1.76 g/cc |
0.0636 lb/in³ |
| Water Absorption |
<= 0.0400 % |
<= 0.0400 % |
| Linear Mold Shrinkage |
0.0200 - 0.0300 cm/cm |
0.0200 - 0.0300 in/in |
Melt Flow  |
5.00 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
5.00 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| |
15.0 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
15.0 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Shore D |
63.0
@Thickness 2.00 mm |
63.0
@Thickness 0.0787 in |
| Tensile Strength, Ultimate |
14.0 - 30.0 MPa |
2030 - 4350 psi |
| Tensile Strength, Yield |
14.0 - 35.0 MPa |
2030 - 5080 psi |
| Elongation at Break |
350 - 600 % |
350 - 600 % |
| Elongation at Yield |
10.0 - 12.0 % |
10.0 - 12.0 % |
| Modulus of Elasticity |
0.800 GPa |
116 ksi |
| Flexural Modulus |
0.850 GPa |
123 ksi |
| Flexural Yield Strength |
33.0 MPa |
4790 psi |
| Coefficient of Friction |
0.200 - 0.300 |
0.200 - 0.300 |
| Coefficient of Friction, Static |
0.200 - 0.400 |
0.200 - 0.400 |
| Taber Abrasion, mg/1000 Cycles |
5.00 - 15.0 |
5.00 - 15.0 |
| Izod Impact, Notched |
5.20 J/cm
@Thickness 4.00 mm,
Temperature 23.0 °C |
9.74 ft-lb/in
@Thickness 0.157 in,
Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
>= 1.00e+14 ohm-cm |
>= 1.00e+14 ohm-cm |
| Surface Resistance |
>= 1.00e+14 ohm |
>= 1.00e+14 ohm |
| Dielectric Constant |
7.00
@Frequency 1e+6 Hz |
7.00
@Frequency 1e+6 Hz |
| |
| Thermal Properties |
Metric |
English |
Comments |
| Heat of Fusion |
32.0 J/g |
13.8 BTU/lb |
| |
34.0 J/g |
14.6 BTU/lb |
| CTE, linear |
130 - 150 µm/m-°C
@Temperature 20.0 °C |
72.2 - 83.3 µin/in-°F
@Temperature 68.0 °F |
| Specific Heat Capacity |
1.20 J/g-°C |
0.287 BTU/lb-°F |
| |
1.60 J/g-°C
@Temperature 100 °C |
0.382 BTU/lb-°F
@Temperature 212 °F |
| Thermal Conductivity |
0.180 W/m-K |
1.25 BTU-in/hr-ft²-°F |
| Melting Point |
169 °C |
336 °F |
| Crystallization Temperature |
127 °C |
261 °F |
| Maximum Service Temperature, Air |
320 - 350 °C |
608 - 662 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
82.0 °C
@Thickness 4.00 mm |
180 °F
@Thickness 0.157 in |
| Deflection Temperature at 1.8 MPa (264 psi) |
48.0 °C
@Thickness 4.00 mm |
118 °F
@Thickness 0.157 in |
| Vicat Softening Point |
140 °C
@Load 1.00 kg,
Thickness 4.00 mm |
284 °F
@Load 2.20 lb,
Thickness 0.157 in |
| Brittleness Temperature |
-30.0 °C |
-22.0 °F |
| Glass Transition Temp, Tg |
-30.0 °C |
-22.0 °F |
| Oxygen Index |
46.0 - 65.0 %
@Thickness 3.00 mm |
46.0 - 65.0 %
@Thickness 0.118 in |