| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率190℃/2.16kgISO 113317g/10min |
| 熔体流动速率ASTM D123817g/10min |
| 吸水率24 hrASTM D5700.2% |
| 物理性能比重ASTM D792,ISO 11831.42g/cm3 |
| 成型收缩率FlowASTM D955,ISO 294-41.8-2.2% |
| 成型收缩率Across FlowISO 294-41.8-2.2% |
| 机械性能拉伸模量ISO 527-23000MPa |
| 屈服拉伸应力ISO 527-272MPa |
| 拉伸应力ASTM D63868MPa |
| 断裂伸长率ASTM D63850% |
| 断裂伸长率ISO 527-240% |
| 弯曲模量ASTM D7902940MPa |
| 弯曲强度ASTM D790103MPa |
| charpy缺口冲击强度23℃ISO 179/1eA9kJ/m2 |
| Izod 缺口冲强度ASTM D25669J/m |
| 热性能热变形温度0.45MPa,unannealedISO 75-2/B163℃ |
| 热变形温度1.8MPa,unannealedISO 75-2/A96℃ |
| 阻燃等级UL 94HB |