| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率190℃/2.16kgASTM D123822g/10min |
| 吸水率SaturationASTM D5700.2% |
| 物理性能比重ASTM D7921.42g/cm3 |
| 成型收缩率FlowASTM D9551.8-2.2% |
| 洛氏硬度M-ScaleASTM D78592 |
| 洛氏硬度R-ScaleASTM D785120 |
| 机械性能拉伸强度ASTM D63863.7MPa |
| 断裂伸长率ASTM D63860% |
| 弯曲模量ASTM D7902840MPa |
| 弯曲强度ASTM D79093.2MPa |
| Izod 缺口冲强度ASTM D25668.6J/m |
| 电气性能耐电弧性3.12mmASTM D495150sec |
| 热性能热变形温度0.45MPa,unannealedASTM D648172℃ |
| 热变形温度1.8MPa,unannealedASTM D648125℃ |
| 融化温度179℃ |
| 流动方向线性热膨胀系数ASTM D6960.0001cm/cm/℃ |
| 阻燃等级0.76mmUL 94HB |