| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率ASTM D123830g/10min |
| 熔体流动速率190℃/2.16kgISO 113330g/10min |
| 吸水率24 hrASTM D5700.2% |
| 物理性能比重ASTM D792,ISO 11831.41g/cm3 |
| 成型收缩率FlowASTM D955,ISO 294-41.6-2% |
| 成型收缩率Across FlowISO 294-41.6-2% |
| 机械性能拉伸模量ISO 527-23200MPa |
| 屈服拉伸应力ISO 527-271MPa |
| 拉伸应力ASTM D63865MPa |
| 断裂伸长率ASTM D63850% |
| 断裂伸长率ISO 527-245% |
| 弯曲模量ASTM D7902990MPa |
| 弯曲强度ASTM D79098MPa |
| charpy缺口冲击强度23℃ISO 179/1eA5kJ/m2 |
| Izod 缺口冲强度ASTM D25659J/m |
| 热性能热变形温度0.45MPa,unannealedASTM D648163℃ |
| 热变形温度0.45MPa,unannealedISO 75-2/B161℃ |
| 热变形温度1.8MPa,unannealedASTM D648124℃ |
| 热变形温度1.8MPa,unannealedISO 75-2/A107℃ |
| 阻燃等级UL 94HB |