| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率ASTM D123834g/10min |
| 熔体流动速率190℃/2.16kgISO 113334g/10min |
| 吸水率24 hrASTM D5700.2% |
| 物理性能比重ASTM D792,ISO 11831.42g/cm3 |
| 成型收缩率FlowASTM D955,ISO 294-41.8-2.2% |
| 成型收缩率Across FlowISO 294-41.8-2.2% |
| 机械性能拉伸模量ISO 527-23200MPa |
| 屈服拉伸应力ISO 527-265MPa |
| 拉伸应力ASTM D63861MPa |
| 断裂伸长率ASTM D63840% |
| 断裂伸长率ISO 527-230% |
| 弯曲模量ASTM D7903140MPa |
| 弯曲强度ASTM D79098MPa |
| charpy缺口冲击强度23℃ISO 179/1eA6kJ/m2 |
| Izod 缺口冲强度ASTM D25649J/m |
| 热性能热变形温度0.45MPa,unannealedISO 75-2/B165℃ |
| 热变形温度1.8MPa,unannealedISO 75-2/A100℃ |
| 流动方向线性热膨胀系数ASTM E8310.0001cm/cm/℃ |
| 阻燃等级UL 94HB |