| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能比重ASTM D792, ISO 11831.42g/cm³ |
| 熔体质量流动速率ASTM D12382.8g/10 min |
| 熔体质量流动速率190℃/2.16kgISO 11332.8g/10 min |
| 成型收缩率flowASTM D955, ISO 294-41.8 to 2.2% |
| 成型收缩率Across flowISO 294-41.8 to 2.2% |
| 吸水率24hrASTM D5700.20% |
| 洛氏硬度M-ScaleASTM D78594 |
| 洛氏硬度R-ScaleASTM D785120 |
| 机械性能拉伸模量ISO 527-23100MPa |
| 拉伸应力YieldISO 527-271.0MPa |
| 拉伸应力ASTM D63868.0MPa |
| 拉伸伸长率BreakASTM D63875% |
| 拉伸伸长率BreakISO 527-265% |
| 弯曲模量ASTM D7902740MPa |
| 弯曲强度ASTM D79098.0MPa |
| 泰伯磨耗量1000次ASTM D104413.0mg |
| 夏比缺口冲击强度23°CISO 179/1eA13kJ/m² |
| Izod缺口冲击强度ASTM D256108J/m |
| 热性能热畸变温度0.45MPa,未退火ASTM D648172°C |
| 热畸变温度1.8MPa,未退火ASTM D648133°C |
| 热畸变温度0.45MPa,未退火ISO 75-2/B163°C |
| 热畸变温度1.8MPa,未退火ISO 75-2/A96.0°C |
| 线性热膨胀系数flowASTM E8310.00010cm/cm/°C |
| 其它性能阻燃等级UL 94HB |