| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 物理性能吸水均衡性50% RHL;DAMSimilar to ISO 622.6% |
| 粘性系数测试Viscosity Number;DAMISO 307275cm3/g |
| 吸水饱和性-DAMASTM D5708.5% |
| -DAMSimilar to ISO 628.5% |
| 密度-DAMASTM D7921.14g/cc |
| -DAMISO 11831.14g/cc |
| 线型模量收缩率横向2.0mm;DAMISO 294-40.014cm/cm |
| 线型模量收缩率-Parallel;2.0mm;DAMISO 294-40.014cm/cm |
| -Flow;3.2mm(0.126in);DAMISO 294-40.015cm/cm |
| 吸水率immersion 24h;DAMASTM D5701.2% |
| 机械性能Charpy缺口冲击-DAMISO 179/1eA0.6J/cm2 |
| -50% RHISO 179/1eA2J/cm2 |
| 低温下charpy缺口冲击--30℃；50% RHISO 179/1eU0.4J/cm2 |
| --30℃；DAMISO 179/1eU0.6J/cm2 |
| 拉伸屈服强度-50% RHISO 52755MPa |
| -50% RHASTM D63859MPa |
| -DAMISO 52783MPa |
| 弯曲模量-50% RHISO 1781.07GPa |
| -50% RHASTM D7901.21GPa |
| -DAMISO 1782.8GPa |
| -DAMASTM D7902.83GPa |
| 洛氏硬度-DAMASTM D78580M |
| -DAMASTM D785121R |
| 拉伸模量-50% RHISO 5271.3GPa |
| -DAMISO 5273.1GPa |
| 低温下charpy抗冲击强度--30℃；50% RHISO 179/1eUNB- |
| --30℃；DAMISO 179/1eUNB- |
| Charpy抗冲击强度-50% RHISO 179/1eUNB- |
| -DAMISO 179/1eUNB- |
| IZOD冲击-DAMASTM D2560.64J/cm |
| -50% RHASTM D2561.33J/cm |
| 拉伸率-50% RHASTM D63830% |
| -DAMISO 5274.4% |
| -DAMASTM D6385% |
| IZOD缺口冲击-50% RHISO 180/1A23KJ/m2 |
| -DAMISO 180/1A6KJ/m2 |
| IZOD抗冲击强度-DAMISO 180/1UNB- |
| -50% RHISO 180/1UNB- |
| 拉力抗冲强度Long specimen;DAMASTM D1822535KJ/m2 |
| 纯强度-50% RHASTM D73263MPa |
| -DAMASTM D73266MPa |
| IZOD抗冲-50% RHASTM D2560.27J/cm |
| -DAMASTM D2560.32J/cm |
| 拉伸强度-50% RHASTM D63877MPa |
| -DAMASTM D63885MPa |
| 电气性能体积电阻率-50% RHIEC 600931e+011ohm-cm |
| -DAMIEC 600931e+013ohm-cm |
| 介电常数-1MHz;50%RHIEC 602504.2- |
| -100Hz;DAMIEC 602504.3- |
| -50%RHASTM D1504.6- |
| -50%RHASTM D1507- |
| -50%RHASTM D1508- |
| 介电常数-100Hz;50%RHIEC 6025010.03- |
| -DAMASTM D1503.6- |
| -MHz;DAMIEC 602503.6- |
| -DAMASTM D1503.9- |
| -DAMASTM D1504- |
| 介电损耗因素-100Hz;DAMASTM D1500.01- |
| -100Hz;DAMIEC 602500.015- |
| -1KHz;DAMASTM D1500.02- |
| -1MHz;DAMASTM D1500.02- |
| 加工性能熔融温度DAM280-300℃ |
| 干燥损失率DAMMax0.05% |
| 模量温度DAM50-90℃ |
| 热性能ULRTI，机械性-3.0mm;DAMUL 746B85℃ |
| -1.5MM;DAMUL 746B85℃ |
| 热膨胀系数线型20℃下横流23-55℃(73-130°F);DAMASTM E831100μm/m-℃ |
| 线型20℃下横流23-55℃(73-130°F);DAMISO 11359-1/-2100μm/m-℃ |
| ULRTI，电气性-3.0mm;DAMUL 746B125℃ |
| -1.5MM;DAMUL 746B125℃ |
| 氧气指数DAMISO 4589-1/-228% |
| 脆化温度DAMASTM D746-100℃ |
| 熔点-10℃/min;DAMISO 11357-1-3262℃ |
| -DAMASTM D3418263℃ |
| 变形温度-at 0.46 MPaISO 75-1/-2200℃ |
| -at 0.46 MPaASTM D648210℃ |
| -at 1.8 MPaASTM D64865℃ |
| -at 1.8 MPaISO 75-1/-270℃ |
| 燃烧性-1.5mm;DAMUL 94HB- |
| -1.5mm;DAMIEC 60695-11-10HB- |
| -0.71mm;DAMIEC 60695-11-10HB- |
| -0.71mm;DAMUL 94HB- |
| -3.0mm;DAMIEC 60695-11-10HB- |
| -3.0mm;DAMUL 94HB- |
| 热膨胀系数线型20℃Parallel;23-55℃(73-130°F);DAMASTM E831100μm/m-℃ |
| 线型20℃Parallel;23-55℃(73-130°F);DAMISO 11359-1/-2100μm/m-℃ |
| ULRTI,抗冲性机械性能-1.5mm;DAMUL 746B75℃ |
| -3.0mm;DAMUL 746B75℃ |
| 其它性能颜色天然 |
| 形式粒子 |
| 加工方法---注塑成型- |
| ---挤出- |
| ---注塑- |
| ---涂层- |