| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能吸水率饱和(23℃)ASTM D-5705.4% |
| 吸水率24小时浸渍(23℃)ASTM D-5700.7% |
| 物理性能比重ASTM D-7921.38 |
| 机械性能断裂伸长率23℃,DAMASTM D-6383% |
| 断裂伸长率23℃,50%RHASTM D-6384% |
| 拉伸强度23℃,DAMASTM D-638196.1MPa |
| 挠曲模量23℃,50%RHASTM D-7906205MPa |
| 拉伸强度23℃,50%RHASTM D-638124.1MPa |
| 洛氏硬度MDAMASTM D-785M101 |
| 挠曲模量23℃,DAMASTM D-7908963MPa |
| 挤剪强度23℃,DAMASTM D-73286MPa |
| 泰伯磨耗量50%RH14cycles |
| 埃佐冲击强度23℃,DAMASTM D-256107j/m |
| 埃佐冲击强度23℃,50%RHASTM D-256133j/m |
| 挠曲强度23℃,DAMASTM D-790262MPa |
| 电气性能介电强度(分步法)DAMASTM D-149440volts/mil |
| 介电常数100%RH@106Hz赫ASTM D-15010.7 |
| 介电常数100%RH@103Hz赫ASTM D-15025.0 |
| 体积电阻率100%RHASTM D-257109ohm-cm |
| 介电常数DAM@106Hz赫ASTM D-1503.7 |
| 介电强度DAMASTM D-149530volts/mil |
| 损耗因数DAM@103Hz赫ASTM D-1500.02 |
| 体积电阻率DAMASTM D-2571015ohm-cm |
| 介电常数DAM@103Hz赫ASTM D-1504.5 |
| 损耗因数DAM@106Hz赫ASTM D-1500.02 |
| 热性能热畸变温度1.8MPaASTM D-648249℃ |
| 熔点50%RHASTM D-789255℃ |
| 熔点ASTM D-789DAM255℃ |
| 线性热膨胀系数ASTM D-6962.3×10-5m/m/℃ |