| Physical Properties |
Metric |
English |
Comments |
| Specific Gravity |
1.02 g/cc |
1.02 g/cc |
| Density |
1.02 g/cc |
0.0368 lb/in³ |
| Water Absorption |
0.420 % |
0.420 % |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Shore D |
55.0 |
55.0 |
| Tensile Strength, Ultimate |
7.00 MPa
@Temperature 120 °C |
1020 psi
@Temperature 248 °F |
| |
7.00 MPa
@Temperature 149 °C |
1020 psi
@Temperature 300 °F |
| |
10.0 MPa
@Temperature 77.0 °C |
1450 psi
@Temperature 171 °F |
| |
25.0 MPa
@Temperature 23.0 °C |
3630 psi
@Temperature 73.4 °F |
| |
27.0 MPa
@Temperature 23.0 °C |
3920 psi
@Temperature 73.4 °F |
| |
50.0 MPa
@Temperature -40.0 °C |
7250 psi
@Temperature -40.0 °F |
| Tensile Strength, Yield |
24.5 MPa
@Temperature 23.0 °C |
3550 psi
@Temperature 73.4 °F |
| |
27.2 MPa
@Temperature 23.0 °C |
3950 psi
@Temperature 73.4 °F |
|
13.5 MPa
@Strain 50.0 % |
1960 psi
@Strain 50.0 % |
| |
19.0 MPa
@Strain 50.0 % |
2760 psi
@Strain 50.0 % |
| Elongation at Break |
260 % |
260 % |
| |
292 % |
292 % |
| Tensile Modulus |
0.240 GPa |
34.8 ksi |
| |
0.550 GPa |
79.8 ksi |
| Flexural Modulus |
0.0620 GPa
@Temperature 149 °C |
8.99 ksi
@Temperature 300 °F |
| |
0.0620 GPa
@Temperature 120 °C |
8.99 ksi
@Temperature 248 °F |
| |
0.110 GPa
@Temperature 77.0 °C |
16.0 ksi
@Temperature 171 °F |
| |
0.290 GPa
@Temperature 23.0 °C |
42.1 ksi
@Temperature 73.4 °F |
| |
0.520 GPa
@Temperature 23.0 °C |
75.4 ksi
@Temperature 73.4 °F |
| |
1.17 GPa
@Temperature -40.0 °C |
170 ksi
@Temperature -40.0 °F |
| Tensile Impact Strength |
1200 kJ/m² |
571 ft-lb/in² |
| Izod Impact, Notched |
4.80 J/cm
@Temperature -40.0 °C |
8.99 ft-lb/in
@Temperature -40.0 °F |
| |
NB
@Temperature -29.0 °C |
NB
@Temperature -20.2 °F |
| |
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
| Izod Impact, Notched (ISO) |
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
| |
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Volume Resistivity |
1.00e+13 ohm-cm |
1.00e+13 ohm-cm |
| |
>= 1.00e+15 ohm-cm |
>= 1.00e+15 ohm-cm |
| |
1.00e+17 ohm-cm |
1.00e+17 ohm-cm |
| |
| Thermal Properties |
Metric |
English |
Comments |
| Melting Point |
263 °C |
505 °F |
| |
265 °C |
509 °F |
| |
| Processing Properties |
Metric |
English |
Comments |
| Melt Temperature |
285 °C |
545 °F |
| |
275 - 295 °C |
527 - 563 °F |
| Mold Temperature |
60.0 °C |
140 °F |
| |
40.0 - 80.0 °C |
104 - 176 °F |
| Drying Temperature |
80.0 °C |
176 °F |
| Dry Time |
2 - 4 hour |
2 - 4 hour |
| Moisture Content |
<= 0.200 % |
<= 0.200 % |
| |
| Descriptive Properties |
| Additive |
Antioxidant |
| |
Impact Modifier |
| |
Lubricant |
| Color |
Natural |
| Drying Recommended |
Yes, if moisture content of resin exceeds recommended level |
| Features |
Antioxidant |
| |
Flexibility, Good |
| |
Impact Modified |
| |
Impact Resistance, Good |
| |
Lubricated |
| Forms |
Pellets |
| Generic |
Nylon 66 |
| Part Marking Code |
>PA66-F< |
| Polymer Family |
Polyamide |
| Polymer Type |
PA66 |
| Processing |
Injection Moldable |
| Processing Method |
Extrusion |
| |
Injection Molding |
| Product Category |
Toughened Resins |
| |
Unreinforced Resins |
| Region Available |
Americas |
| |
Asia/Pacific |
| |
Europe |
| Resin Identification |
PA66-F |
| Uses |