| Physical Properties |
Metric |
English |
Comments |
| Specific Gravity |
1.20 g/cc |
1.20 g/cc |
| Water Absorption |
1.50 %
@Time 86400 sec |
1.50 %
@Time 24.0 hour |
| Linear Mold Shrinkage |
0.00200 - 0.00600 cm/cm |
0.00200 - 0.00600 in/in |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Rockwell R |
81.0 |
81.0 |
| Tensile Strength at Break |
34.5 MPa |
5000 psi |
| Tensile Strength, Yield |
33.3 MPa |
4830 psi |
| Elongation at Break |
45.0 % |
45.0 % |
| Flexural Modulus |
1.52 GPa |
220 ksi |
| Flexural Strength |
43.7 MPa |
6340 psi |
| Izod Impact, Notched |
1.03 J/cm
@Temperature -40.0 °C |
1.93 ft-lb/in
@Temperature -40.0 °F |
| |
3.53 J/cm
@Temperature 23.0 °C |
6.61 ft-lb/in
@Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Volume Resistivity |
1.00e+13 - 1.00e+15 ohm-cm |
1.00e+13 - 1.00e+15 ohm-cm |
| Dielectric Constant |
3.30 - 3.80
@Frequency 1.00e+6 Hz |
3.30 - 3.80
@Frequency 1.00e+6 Hz |
| Dissipation Factor |
0.0100 - 0.150
@Frequency 1.00e+6 Hz |
0.0100 - 0.150
@Frequency 1.00e+6 Hz |
| |
| Thermal Properties |
Metric |
English |
Comments |
| CTE, linear |
110 - 170 µm/m-°C |
61.1 - 94.4 µin/in-°F |
| Specific Heat Capacity |
1.26 - 1.67 J/g-°C |
0.301 - 0.399 BTU/lb-°F |
| Thermal Conductivity |
0.170 - 0.330 W/m-K |
1.18 - 2.29 BTU-in/hr-ft²-°F |
| Deflection Temperature at 0.46 MPa (66 psi) |
85.0 °C |
185 °F |
| Deflection Temperature at 1.8 MPa (264 psi) |
76.0 °C |
169 °F |
| Vicat Softening Point |
98.0 °C |
208 °F |
| |
| Optical Properties |
Metric |
English |
Comments |
| Refractive Index |
1.46 - 1.49 |
1.46 - 1.49 |
| Haze |
<= 8.50 % |
<= 8.50 % |
| Transmission, Visible |
>= 90.0 % |
>= 90.0 % |
| |
| Descriptive Properties |
| Formula Number |
383 |
| Plasticizer |
11 percent |
| Soluble Matter Loss |
0.1 percent |
| Weight Loss on Heating |
0.4 percent |