| Physical Properties |
Metric |
English |
Comments |
| Density |
1.21 g/cc |
0.0437 lb/in³ |
| Water Absorption |
1.60 % |
1.60 % |
| Linear Mold Shrinkage |
0.00400 cm/cm |
0.00400 in/in |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Rockwell R |
90 |
90 |
| Tensile Strength, Ultimate |
40.0 MPa |
5800 psi |
| Tensile Strength, Yield |
37.2 MPa |
5400 psi |
| Elongation at Break |
45.0 % |
45.0 % |
| Flexural Modulus |
1.655 GPa |
240.0 ksi |
| Flexural Yield Strength |
48.3 MPa |
7010 psi |
| Izod Impact, Notched |
2.25 J/cm |
4.22 ft-lb/in |
|
0.960 J/cm
@Temperature -40.0 °C |
1.80 ft-lb/in
@Temperature -40.0 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
1.00e+13 - 1.00e+15 ohm-cm |
1.00e+13 - 1.00e+15 ohm-cm |
| Dielectric Constant |
3.55
@Frequency 1e+6 Hz |
3.55
@Frequency 1e+6 Hz |
| Dielectric Strength |
15.25 kV/mm |
387.4 kV/in |
| Dissipation Factor |
0.0800
@Frequency 1e+6 Hz |
0.0800
@Frequency 1e+6 Hz |
| |
| Thermal Properties |
Metric |
English |
Comments |
| CTE, linear |
11.0 - 17.0 µm/m-°C
@Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F
@Temperature 68.0 °F |
| Specific Heat Capacity |
1.465 J/g-°C |
0.3501 BTU/lb-°F |
| Thermal Conductivity |
0.250 W/m-K |
1.74 BTU-in/hr-ft²-°F |
| Deflection Temperature at 0.46 MPa (66 psi) |
88.0 °C |
190 °F |
| Deflection Temperature at 1.8 MPa (264 psi) |
80.0 °C |
176 °F |
| Vicat Softening Point |
105 °C |
221 °F |
| |
| Optical Properties |
Metric |
English |
Comments |
| Refractive Index |
1.475 |
1.475 |
| Haze |
<= 8.50 %
@Thickness 1.52 mm |
<= 8.50 %
@Thickness 0.0598 in |
| Transmission, Visible |
>= 90.0 %
@Thickness 1.52 mm |
>= 90.0 %
@Thickness 0.0598 in |