| Physical Properties |
Metric |
English |
Comments |
| Density |
1.20 g/cc |
0.0434 lb/in³ |
| Water Absorption |
1.50 % |
1.50 % |
| Linear Mold Shrinkage |
0.00400 cm/cm |
0.00400 in/in |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Rockwell R |
80 |
80 |
| Tensile Strength, Ultimate |
36.5 MPa |
5290 psi |
| Tensile Strength, Yield |
31.7 MPa |
4600 psi |
| Elongation at Break |
40.0 % |
40.0 % |
| Flexural Modulus |
1.517 GPa |
220.0 ksi |
| Flexural Yield Strength |
41.4 MPa |
6000 psi |
| Izod Impact, Notched |
4.16 J/cm |
7.79 ft-lb/in |
|
1.07 J/cm
@Temperature -40.0 °C |
2.00 ft-lb/in
@Temperature -40.0 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
1.00e+13 - 1.00e+15 ohm-cm |
1.00e+13 - 1.00e+15 ohm-cm |
| Dielectric Constant |
3.55
@Frequency 1e+6 Hz |
3.55
@Frequency 1e+6 Hz |
| Dielectric Strength |
15.25 kV/mm |
387.4 kV/in |
| Dissipation Factor |
0.0800
@Frequency 1e+6 Hz |
0.0800
@Frequency 1e+6 Hz |
| |
| Thermal Properties |
Metric |
English |
Comments |
| CTE, linear |
11.0 - 17.0 µm/m-°C
@Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F
@Temperature 68.0 °F |
| Specific Heat Capacity |
1.465 J/g-°C |
0.3501 BTU/lb-°F |
| Thermal Conductivity |
0.250 W/m-K |
1.74 BTU-in/hr-ft²-°F |
| Deflection Temperature at 0.46 MPa (66 psi) |
84.0 °C |
183 °F |
| Deflection Temperature at 1.8 MPa (264 psi) |
76.0 °C |
169 °F |
| Vicat Softening Point |
100 °C |
212 °F |
| |
| Optical Properties |
Metric |
English |
Comments |
| Refractive Index |
1.475 |
1.475 |
| Haze |
<= 8.50 %
@Thickness 1.52 mm |
<= 8.50 %
@Thickness 0.0598 in |
| Transmission, Visible |
>= 90.0 %
@Thickness 1.52 mm |
>= 90.0 %
@Thickness 0.0598 in |