Physical Properties
Metric
English
Comments
| Density |
1.20g/cc |
0.0434lb/in³ |
| Linear Mold Shrinkage, Flow |
0.00200-0.00600cm/cm
@Thickness 3.20 mm |
0.00200-0.00600in/in
@Thickness 0.126 in |
| |
Mechanical Properties
Metric
English
Comments
| Tensile Strength, Yield |
34.0MPa |
4930psi |
| Elongation at Break |
37.0 % |
37.0 % |
| Elongation at Yield |
4.00 % |
4.00 % |
| Tensile Modulus |
1.78GPa |
258ksi |
| Charpy Impact Unnotched |
NB |
NB |
|
NB
@Temperature -30.0 °C |
NB
@Temperature -22.0 °F |
| Charpy Impact, Notched |
1.62J/cm² |
7.71ft-lb/in² |
|
0.780J/cm²
@Temperature -30.0 °C |
3.71ft-lb/in²
@Temperature -22.0 °F |
| |
Thermal Properties
Metric
English
Comments
| CTE, linear |
93.0µm/m-°C
@Temperature 20.0 °C |
51.7µin/in-°F
@Temperature 68.0 °F |
| CTE, linear, Transverse to Flow |
137µm/m-°C
@Temperature 20.0 °C |
76.1µin/in-°F
@Temperature 68.0 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0°C |
199°F |
| Deflection Temperature at 1.8 MPa (264 psi) |
85.0°C |
185°F |
| Vicat Softening Point |
92.0°C |
198°F |
| Glass Transition Temp, Tg |
105°C |
221°F |