Physical Properties
Metric
English
Comments
| Density |
1.19g/cc |
0.0430lb/in³ |
| Linear Mold Shrinkage, Flow |
0.00200-0.00600cm/cm
@Thickness 3.20 mm |
0.00200-0.00600in/in
@Thickness 0.126 in |
| |
Mechanical Properties
Metric
English
Comments
| Tensile Strength, Yield |
28.0MPa |
4060psi |
| Elongation at Break |
34.0 % |
34.0 % |
| Elongation at Yield |
3.70 % |
3.70 % |
| Tensile Modulus |
1.41GPa |
205ksi |
| Charpy Impact Unnotched |
NB |
NB |
|
NB
@Temperature -30.0 °C |
NB
@Temperature -22.0 °F |
| Charpy Impact, Notched |
2.61J/cm² |
12.4ft-lb/in² |
|
0.720J/cm²
@Temperature -30.0 °C |
3.43ft-lb/in²
@Temperature -22.0 °F |
| |
Thermal Properties
Metric
English
Comments
| CTE, linear |
112µm/m-°C
@Temperature 20.0 °C |
62.2µin/in-°F
@Temperature 68.0 °F |
| CTE, linear, Transverse to Flow |
133µm/m-°C
@Temperature 20.0 °C |
73.9µin/in-°F
@Temperature 68.0 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
86.0°C |
187°F |
| Deflection Temperature at 1.8 MPa (264 psi) |
77.0°C |
171°F |
| Vicat Softening Point |
81.0°C |
178°F |
| Glass Transition Temp, Tg |
90.0°C |
194° |