Physical Properties
Metric
English
Comments
| Specific Gravity |
1.19g/cc |
1.19g/cc |
| Water Absorption |
1.40 % |
1.40 % |
| Linear Mold Shrinkage |
0.00200-0.00600cm/cm |
0.00200-0.00600in/in |
| Collected Volatile Condensable Material |
1.30 % |
1.30 % |
| |
Mechanical Properties
Metric
English
Comments
| Tensile Strength at Break |
30.3MPa |
4390psi |
| Tensile Strength, Yield |
26.9MPa |
3900psi |
| Elongation at Break |
45.0 % |
45.0 % |
| Flexural Modulus |
1.241GPa |
180.0ksi |
| Flexural Yield Strength |
35.2MPa |
5110psi |
| Izod Impact, Notched |
1.23J/cm
@Temperature -40.0 °C |
2.30ft-lb/in
@Temperature -40.0 °F |
| |
>=5.33J/cm
@Temperature 23.0 °C |
>=9.99ft-lb/in
@Temperature 73.4 °F |
| |
Electrical Properties
Metric
English
Comments
| Volume Resistivity |
1.00e+13-1.00e+15ohm-cm |
1.00e+13-1.00e+15ohm-cm |
| Dielectric Constant |
3.30 - 3.80
@Frequency 1e+6 Hz |
3.30 - 3.80
@Frequency 1e+6 Hz |
| Dielectric Strength |
11.8-18.7kV/mm |
300-475kV/in |
| Dissipation Factor |
0.0100 - 0.150
@Frequency 1e+6 Hz |
0.0100 - 0.150
@Frequency 1e+6 Hz |
| |
Thermal Properties
Metric
English
Comments
| CTE, linear |
110-170µm/m-°C
@Temperature 20.0 °C |
61.1-94.4µin/in-°F
@Temperature 68.0 °F |
| Specific Heat Capacity |
1.26-1.67J/g-°C |
0.301-0.399BTU/lb-°F |
| Thermal Conductivity |
0.170-0.330W/m-K |
1.18-2.29BTU-in/hr-ft²-°F |
| Deflection Temperature at 0.46 MPa (66 psi) |
80.0°C |
176°F |
| Deflection Temperature at 1.8 MPa (264 psi) |
72.0°C |
162°F |
| Vicat Softening Point |
92.0°C |
198°F |