Physical Properties
Metric
English
Comments
| Specific Gravity |
1.20g/cc |
1.20g/cc |
| Water Absorption |
1.50 %
@Time 86400 sec |
1.50 %
@Time 24.0 hour |
| Linear Mold Shrinkage |
0.00200-0.00600cm/cm |
0.00200-0.00600in/in |
| |
Mechanical Properties
Metric
English
Comments
| Hardness, Rockwell R |
73.0 |
73.0 |
| Tensile Strength at Break |
31.7MPa |
4600psi |
| Tensile Strength, Yield |
29.3MPa |
4250psi |
| Elongation at Break |
45.0 % |
45.0 % |
| Flexural Modulus |
1.345GPa |
195.1ksi |
| Flexural Strength |
38.3MPa |
5550psi |
| Izod Impact, Notched |
1.15J/cm
@Temperature -40.0 °C |
2.15ft-lb/in
@Temperature -40.0 °F |
| |
4.75J/cm
@Temperature 23.0 °C |
8.90ft-lb/in
@Temperature 73.4 °F |
| |
Electrical Properties
Metric
English
Comments
| Volume Resistivity |
1.00e+13-1.00e+15ohm-cm |
1.00e+13-1.00e+15ohm-cm |
| Dielectric Constant |
3.30 - 3.80
@Frequency 1.00e+6 Hz |
3.30 - 3.80
@Frequency 1.00e+6 Hz |
| Dielectric Strength |
11.8-18.7kV/mm |
300-475kV/in |
| Dissipation Factor |
0.0100 - 0.150
@Frequency 1.00e+6 Hz |
0.0100 - 0.150
@Frequency 1.00e+6 Hz |
| |
Thermal Properties
Metric
English
Comments
| CTE, linear |
110-170µm/m-°C |
61.1-94.4µin/in-°F |
| Specific Heat Capacity |
1.26-1.67J/g-°C |
0.301-0.399BTU/lb-°F |
| Thermal Conductivity |
0.170-0.330W/m-K |
1.18-2.29BTU-in/hr-ft²-°F |
| Deflection Temperature at 0.46 MPa (66 psi) |
82.0°C |
180°F |
| Deflection Temperature at 1.8 MPa (264 psi) |
74.0°C |
165°F |
| Vicat Softening Point |
94.0°C |
201°F |