| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 物理性能熔融指数260℃,5kgASTM D-123830g/10min |
| 密度ASTM D-15051.08g/cm3 |
| 熔点MCI方法240℃ |
| 机械性能抗张强度ASTM D-638170kg/cm2 |
| 凹口Charpy耐冲击强度ASTM D-256---kgcm/cm2 |
| 断裂伸长率ASTM D-63825% |
| 曲折模数ASTM D-79019,000kg/cm2 |
| 抗张屈服强度ASTM D-638240kg/cm2 |
| Rockwell硬度ASTM D-785R90 |
| 无凹口lzod耐冲击强度ASTM D-256--kgcm/cm2 |
| 曲折强度ASTM D-790390kg/cm2 |
| Olsen刚性ASTM D-747---kg/cm2 |
| 电气性能介电常数100～1MHzASTM D-150--- |
| 吸水率24hrASTM D-5700.11% |
| 介电强度ASTM D-149---KV/mm |
| 体积电阻系数ASTM D-257---Ωcm |
| 介电消散因子23℃,1MHzASTM D-1500.0014 |
| 热性能比热ASTM C-351---cal/g℃ |
| 燃烧速率ASTM D-635---cm/min |
| Vicat软化点ASTM D-1525175℃ |
| 热变形温度4.6kg/cm2ASTM D-648110℃ |
| 热传导系数ASTM BS-847A---calcm/seccm2℃ |
| 模收缩率(机械/垂直方向)MCI方法1.7/1.4% |
| 线膨胀系数ASTM D-696---1/℃ |
| 其它性能折射率ASTM D-542---nd |
| 模糊度ASTM D-1746---% |
| 透光率ASTM D-1746---% |