| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 物理性能熔点MCI方法235℃ |
| 密度ASTM D-15050.833g/cm3 |
| 熔融指数(260℃，5kg)ASTM D-123821g/10min |
| 机械性能Rockwell硬度ASTM D-785R90 |
| 拉伸模量ASTM D-6381865MPa |
| 拉伸强度ASTM D-63820MPa |
| 弹性强度ASTM D-79051MPa |
| 断裂伸长率ASTM D-63832% |
| 屈服拉伸强度ASTM D-63826MPa |
| Izod 耐冲击强度ASTM D-25610KJ/m2 |
| 弹性模量ASTM D-7901765MPa |
| 电气性能介电常数 (100～1MHz)ASTM D-1502.12 |
| 介电强度ASTM D-14965KV/mm |
| 吸水率(24hr)ASTM D-5700.01% |
| 体积电阻系数ASTM D-257>1016Ωcm |
| 介电消散因子 (23℃, 1MHz)ASTM D-1500.0007 |
| 热性能模收缩率(纵向/横向)MCI方法2.1/1.7% |
| 热传导系数ASTM BS-847A4*10-4calcm/seccm2℃ |
| 燃烧速率ASTM D-6352.54cm/min |
| 比热ASTM C-3510.47cal/g℃ |
| 热变形温度 (4.6kg/cm2)ASTM D-64890℃ |
| Vicat软化点ASTM D-1525177℃ |
| 线性膨胀系数ASTM D-6961.17*10-41/℃ |
| 其它性能模糊度ASTM D-17462.6% |
| 透光率ASTM D-174693% |
| 折射率ASTM D-5421.463nd |