Tensile Stress, break

1230

kgf/cm²

ASTM D 638

Tensile Strain, break

0.8

%

ASTM D 638

Tensile Modulus, 50 mm/min

234100

kgf/cm²

ASTM D 638

Flexural Stress

2580

kgf/cm²

ASTM D 790

Flexural Modulus

250200

kgf/cm²

ASTM D 790

Tensile Stress, break

165

MPa

ISO 527

Tensile Strain, break

0.8

%

ISO 527

Tensile Modulus, 1 mm/min

26200

MPa

ISO 527

Flexural Stress

259

MPa

ISO 178

Flexural Modulus

25940

MPa

ISO 178

Izod Impact, unnotched, 23°C

40

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

4

cm-kgf/cm

ASTM D 256

Instrumented Impact Energy @ peak, 23°C

45

cm-kgf

ASTM D 3763

Multiaxial Impact

22

cm-kgf

ISO 6603

Izod Impact, unnotched 80*10*4 +23°C

24

kJ/m²

ISO 180/1U

Izod Impact, notched 80*10*4 +23°C

5

kJ/m²

ISO 180/1A

HDT, 1.82 MPa, 3.2mm, unannealed

269

°C

ASTM D 648

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

265

°C

ISO 75/Af

Density

1.55

g/cm³

ASTM D 792

Moisture Absorption, 50% RH, 24 hrs

0.02

%

ASTM D 570

Mold Shrinkage, flow, 24 hrs (5)

0.1

%

ASTM D 955

Mold Shrinkage, xflow, 24 hrs (5)

0.4

%

ASTM D 955

Mold Shrinkage, flow, 24 hrs (5)

0.06

%

ISO 294

Mold Shrinkage, xflow, 24 hrs (5)

0.44

%

ISO 294

Wear Factor Washer

47

10^-10 in^5-min/ft-lb-hr

ASTM D 3702 Modified

Dynamic COF

0.36

-

ASTM D 3702 Modified

Static COF

0.31

-

ASTM D 3702 Modified

Density

1.55

g/cm³

ISO 1183

Moisture Absorption (23°C / 50% RH)

0.02

%

ISO 62