| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率ASTM D123830g/10min |
| 熔体流动速率190℃/2.16kgISO 113330g/10min |
| 吸水率24 hrASTM D5700.2% |
| 物理性能比重ASTM D792,ISO 11831.41g/cm3 |
| 成型收缩率FlowASTM D9551.5-1.9% |
| 成型收缩率Across FlowISO 294-41.6-2% |
| 成型收缩率FlowISO 294-41.6-2% |
| 洛氏硬度M-ScaleASTM D78580 |
| 洛氏硬度R-ScaleASTM D785115 |
| 机械性能拉伸模量ISO 527-22850MPa |
| 屈服拉伸应力ISO 527-266MPa |
| 拉伸应力ASTM D63860MPa |
| 断裂伸长率ASTM D63850% |
| 断裂伸长率ISO 527-230% |
| 弯曲模量ASTM D7902630MPa |
| 弯曲强度ASTM D79090MPa |
| 泰伯耐磨性1000 CyclesASTM D104414mg |
| charpy缺口冲击强度23℃ISO 179/1eA4kJ/m2 |
| Izod 缺口冲强度ASTM D25639J/m |
| 热性能热变形温度0.45MPa,unannealedASTM D648158℃ |
| 热变形温度0.45MPa,unannealedISO 75-2/B157℃ |
| 热变形温度1.8MPa,unannealedASTM D648110℃ |
| 热变形温度1.8MPa,unannealedISO 75-2/A100℃ |
| 流动方向线性热膨胀系数ASTM E8310.0001cm/cm/℃ |
| 阻燃等级UL 94HB |